Stress related aspects of GaN technology physics

At a Glance

Metadata	Details
Publication Date	2015-03-13
Journal	Proceedings of SPIE, the International Society for Optical Engineering/Proceedings of SPIE
Authors	E. Suhir
Institutions	Endocrine Research Solutions (United States), Portland State University
Citations	1

Abstract

Simple, easy-to-use and physically meaningful analytical models have been developed for the assessment of the combined effect of the lattice and thermal mismatch on the induced stresses in an elongated bi-material assembly, as well as on the thermal mismatch on the thermal stresses in a tri-material assembly, in which the lattice mismatched stresses are eliminated in one way or another. This could be done, e.g., by using a polished or an etched substrate. The analysis is carried out in application to Gallium Nitride (GaN)-Silicon Carbide (SiC) and GaN-diamond (C) filmsubstrate assemblies. The calculated data are obtained, assuming that no annealing or other stress reduction means is applied. The data agree reasonably well with the reported (available) in-situ measurements. The most important conclusion from the computed data is that even if a reasonably good lattice match takes place (as, e.g., in the case of a GaN film fabricated on a SiC substrate, when the mismatch strain is only about 3%) and, in addition, the temperature change (from the fabrication/growth temperature to the operation temperature) is significant (as high as 1000 ̊C), the thermal stresses are still considerably lower than the lattice-mismatch stresses. Although there are structural and technological means for further reduction of the lattice-mismatch stresses (e.g., by high temperature annealing or by providing one or more buffering layers, or by using patterned or porous substrates), there is still a strong incentive to eliminate completely the lattice mismatch stresses. This seems to be indeed possible, if polished or otherwise flattened (e.g., chemically etched) substrates and sputter deposited GaN film is employed. In such a case only thermal stresses remain, but even these could be reduced, if necessary, by using compliant buffering layers, including layers of variable compliance, or by introducing variable compliance into the properly engineered substrate. In any event, it is expected that strong adhesion could be achieved by using an appropriate fabrication technology, so that no GaN film cracking would be possible, if the film is in tension, or delamination buckling could occur if the film is in compression. The developed models can be used to assess the possibilities and opportunities associated with GaN materials technology.

Tech Support

Original Source

DOI: https://doi.org/10.1117/12.2074963

References

2000 - Dual-gate AlGaN/GaN modulation-doped field-effect transistors with cut-off frequencies fT ≻ 60GHz
2003 - High linearity of class B power amplifiers in GaN HEMT technology
2004 - Strain-relieved, dislocation-free InxGa1-xAs⁄GaAs(001) heterostructure by nanoscale-patterned growth
1997 - Strain determination in heteroepitaxial GaN