Texture for Diamond Wire Sawn Multicrystalline Silicon Wafers by a Vapor Etching Method
At a Glance
Section titled āAt a Glanceā| Metadata | Details |
|---|---|
| Publication Date | 2015-01-01 |
| Journal | ACTA PHOTONICA SINICA |
| Authors | Liu Xiao-me |
| Institutions | Nanchang University |
Abstract
Section titled āAbstractāVapor Etching(VE)was used to etch diamond wire sawn mc-silicon wafers.The vapor was generated from heating the acid mixture solution of HF-HNO3 in the volume ratio of 1:3(the total volume of the solution is 400mL)at 90 ā.The results showed that etching for 15 minutes,saw marks can be removed and lots of small corrosion pits which appeared in big corrosion pits were densely covered with silicon wafer surface,the average size of the corrosion pits was about 1Ī¼m,while that by wet acid etch was over 10Ī¼m.The wafer surface roughness with VE method is actually 3times higher than that with traditional wet acid etching method.The effect of VE is obvious and the reflectivity is low to12.11%.
Tech Support
Section titled āTech SupportāOriginal Source
Section titled āOriginal Sourceā- DOI: None