Defect formation in GaAs/GaNxAs1-x core/shell nanowires
At a Glance
Section titled āAt a Glanceā| Metadata | Details |
|---|---|
| Publication Date | 2016-11-14 |
| Journal | Applied Physics Letters |
| Authors | Jan Eric Stehr, S. L. Chen, Mattias Jansson, Fumitaro Ishikawa, Weimin Chen |
| Institutions | Ehime University, Linkƶping University |
| Citations | 12 |
Abstract
Section titled āAbstractāPhotoluminescence and optically detected magnetic resonance (ODMR) spectroscopies are used to investigate the formation and role of defects in GaAs/GaNxAs1-x core/shell nanowires (NWs) grown by molecular beam epitaxy on Si substrates. Gallium vacancies, which act as non-radiative recombination (NRR) centers, are identified by ODMR. It is shown that the defects are formed in bulk regions, i.e., not on the surface, of the GaNAs shell and that their concentration increases with increasing nitrogen content. Temperature dependent photoluminescence experiments reveal, on the other hand, suppressed thermal quenching of the near-band-edge emission with increasing [N]. This leads to the conclusion that the dominant NRR processes in the studied NWs are governed by surface defects, whereas the role of gallium vacancies in the observed thermally activated NRR is minor.