Microtexturing of TiZrN-Coated Si3N4 cutting inserts for machining nickel alloy
At a Glance
Section titled āAt a Glanceā| Metadata | Details |
|---|---|
| Publication Date | 2025-01-01 |
| Journal | EPJ Web of Conferences |
| Authors | Š. A. Volosova, Anna A. Okunkova, Enver Mustafaev, Khasan I. Gkhashim, Alexander P. Malakhinsky |
Abstract
Section titled āAbstractāInsulating cutting ceramics exhibit outstanding mechanical and thermal properties but have electrical conductivity below the percolation threshold. It does not allow sophisticated shapes to be obtained by diamond grinding and polishing. The developed innovative technique is based on choosing the wear-resistant coating based on the chemical composition of the cutting ceramics and its behaviour at 1000-10 000Ā°C, including changing the electrical conductivity from insulating to conducting level, dissociation/sublimation of its components and forming new conductive compounds during cooling that improves the conductive conditions in the interelectrode gap. Thus, the coating plays a wear-resistant role and serves as a technological asset in shaping methods based on the electrical destruction of the materials under discharges. TiZrN coating was deposited on a Si 3 N 4 cutting insert using the vacuum-plasma method, with a thickness of 3.8-4.0 Ī¼m. The ceramics was microtextured by powder-mixed wire electrical discharge machining in TiO 2 -suspension, d w = 0.25 mm. The coated samples were subjected to adhesion and wear-resistance tests. Failure criterion in machining XH45MBTJuBP alloy was chosen a chamfer of 400 Ī¼m. The durability of the TiZrN-coated Si 3 N 4 ceramic insert was improved by 1.33.