LACVD growth of diamond on gallium nitride substrates with PH3 in recipe

At a Glance

Section titled “At a Glance”
MetadataDetails
Publication Date2025-02-24
JournalFrontiers in Energy Research
AuthorsA.K. Mallik, Kamatchi Jothiramalingam Sankaran, Derese Desta, Paulius Pobedinskas, Rani Mary Joy
AnalysisFull AI Review Included

ERROR: File too large (47.6MB)

View Original Abstract

Integrating chemical vapour deposition (CVD) diamond with GaN material for effective thermal management of the power electronic devices is critical. However, there are issues with CVD processing, like GaN substrate etching under normal CVD diamond growth conditions, which nowadays, is overcome by inserting an intermediate silicon nitride layer of very low thermal conductivity. Unfortunately, such a buffer layer is detrimental to proper heat dissipation. So, the direct growth of diamonds onto GaN substrates is still a relevant research topic. Here, we have used an innovative low-temperature growth process by linear antenna microwave plasma enhanced CVD to overcome such a problem. Other than the normal hydrogen gas CVD recipe, PH 3 gas diluted with hydrogen (1,000 ppm in H 2 ) was added as a doping gas precursor, to dope the diamond lattice with phosphorous atoms, by varying the substrate temperature from 400 o C to 900 o C. PH 3 addition in the precursor gas recipe was found to etch the GaN substrate substantially. The phosphorous atom was found to be present on the surface of the diamond film from their corresponding X-ray photoelectron spectroscopy signal. Raman spectroscopy and scanning electron microscopy images do not reveal GaN substrate damage when pure hydrogen gas was used as a precursor without PH 3 addition. However, there is a relative competition between the GaN substrate decomposition and CVD diamond growth rates when diluted PH 3 gas was used in the precursor gas recipe. At a lower substrate temperature of 400 o C, GaN etching was prevalent, but with a gradual increase in substrate temperature to 900ÂșC, diamond lateral growth was promoted inside the linear antenna CVD reactor, which partially protected the underneath GaN/sapphire heterostructures from decomposition under harsh plasma CVD conditions.

Tech Support

Section titled “Tech Support”

Original Source

Section titled “Original Source”

References

Section titled “References”
  1. 2016 - Control of the in-plane thermal conductivity of ultra-thin nanocrystalline diamond films through the grain and grain boundary properties [Crossref]
  2. 1995 - Polarized Raman spectra in GaN [Crossref]
  3. 2019 - Superconducting diamond on silicon nitride for device applications [Crossref]
  4. 2021 - Thermal stress modelling of diamond on GaN/III-Nitride membranes [Crossref]
  5. 2007 - A review of nucleation, growth and low temperature synthesis of diamond thin films [Crossref]
  6. 2015 - Improved nanodiamond seeding on chromium by surface plasma pretreatment [Crossref]
  7. 2018 - Diamond nucleation and growth on horizontally and vertically aligned Si substrates at low pressure in a linear antenna microwave plasma system [Crossref]
  8. 2017 - On the origin of diamond plates deposited at low temperature [Crossref]
  9. 2014 - 3,000+ hours continuous operation of GaN-on-Diamond HEMTs at 350C channel temperature, semiconductor thermal measurement and management symposium (SEMI-THERM) [Crossref]
  10. 2017 - Linear antenna microwave chemical vapour deposition of diamond films on long-period fiber gratings for bio-sensing applications [Crossref]

Reads Similar to This

Recent progress in deep-depletion diamond metal–oxide–semiconductor field-effect transistors Diamond devices for RF applications Effect of Seed Size, Suspension Recycling and Substrate Pre-Treatment on the CVD Growth of Diamond Coatings