Effect of nitrogen in the properties of diamond-like carbon (DLC) coating on Ti6Al4V substrate
At a Glance
Section titled “At a Glance”| Metadata | Details |
|---|---|
| Publication Date | 2020-06-01 |
| Journal | Materials Research Express |
| Authors | Larissa Solano de Almeida, Alan Roger Moreno de Souza, Lenon H. Costa, Elidiane Cipriano Rangel, Marcos Dorigão Manfrinato |
| Institutions | São Paulo State Technological College, Universidade Federal de São Carlos |
| Citations | 31 |
Abstract
Section titled “Abstract”Abstract The great interest in the study of diamond-like carbon films (a-C:H) is justified by its mechanical and tribological properties. However, the high internal stress of the film results in its difficult adhesion to the metallic substrate, which can be solved by nitrogen incorporation in the a-C:H film, allowing a formed film of lower internal stress. The objective of this work is to evaluate the influence of flow (20, 30 and 40sccm), CH 4 /Ar ratio (90/10 and 70/30) and voltage (400, 500, 600 and 700 V) in the a-C:H formation. For the best condition of the film, we studied the effect of nitrogen incorporation in the hardness and wear resistance of the a-C:H(N), modifying the nitrogen percentage in the treatment at 10% to 60% N 2 . The treatments were carried out in the Ti 6 Al 4 V substrate by DC-PECVD for two hours. For good adhesion of the films on the substrate, a silicon interlayer must be produced. The increase in the voltage above 600 V increases the I D /I G and film thickness, causing its delamination, and the gas ratio did not influence the a-C:H characteristics. The a-C:H film deposited with 30 sccm, 90/10 and 500 V was characterized as a-C:H (hard), with properties such as the hardness of 17 GPa, 30% H, 39% sp 3 and I D /I G ratio of 0.58. Since nitrogen reduced the deposition rate, the total gas flow for the production of a-C:H(N) was performed with 40 sccm. The Raman spectra of a-C:H(N) films showed changes in D band intensity and displacement in relation to the nitrogen-free film spectrum, evidencing the incorporation of nitrogen in the film. The XPS analysis showed the linear increase of the nitrogen incorporation in the a-C:H(N) film with the increase of the amount of the N 2 gas in the treatment, which caused, in general, a decrease in the amount of C-C sp 3 bonding, increasing the adhesion of the film in the substrate and not necessarily the low wear resistance of the formed film.
Tech Support
Section titled “Tech Support”Original Source
Section titled “Original Source”References
Section titled “References”- 2008 - Caracterização do diamante CVD depositado sob atmosfera com adição de baixa concentração de N2
- 2020 - Prediction of a novel carbon allotrope from first-principle calculations: a potential superhard material in monoclinic symmetry [Crossref]
- 2002 - Diamond-like amorphous carbon [Crossref]
- 2000 - Influence of nitrogen on the growth of diamond thin films by microwave plasma assisted chemical vapour deposition
- 2018 - Magnetron-sputtered copper/diamond-like carbon composite thin films with super anti-corrosion properties [Crossref]
- 2003 - Novas fases amorfas de carbono produzidas por irradiação iônica de filmes de C/sub 60/, [alfa]-C e [alfa]-C:H
- 1999 - Diamond-like carbon: state of the art [Crossref]
- 2000 - The cutting performance of diamond and DLC-coated cutting tools [Crossref]